  • PVC film,PVC and Aluminum lamination,121℃EH6060A/B +
  • EH6060A/B

    Type of Adhesive: High Grade, two component solvent based(EA) polyurethane adhesive

    Application EH6060A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE films

    Pre-treated PP /CPP films

    Pre-treated PET films

    Pre-treated PA films,

    Unplasticized PVC films, etc.

    Properties

    EH6060A/B is recommended for high performance lamination. Beside its high heat resistance, it is used for flexible packages which are exposed to retorting(e.g. 121℃/40minutes). Especially for Film/Foil structure.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EH6060A EH6060B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 60±2 60±2
    Viscosity(mPa• s,25℃) 2500±1000 500±200
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      80-120lines                            

    Application Solids                                          25-40%(recommend 30%)                

    Pot Life                                                           8hours by dynamic, 24hour by static       

    Dry Coating weight                                        4.0-5.5gsm                              

    Drying Section Temperature                       50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                             50~80℃ depending on films                 

    Cure Time(before slitting)                            60hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EH6060A(kg) EH6060B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 33.6 25 13.5
    20 4 24 30 16.5
    20 4 17.1 35 23

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EH6060A is 20kg/drum, EH6060B is 4kg/drum.

    4            8

  • Low ViscosityEN1175A/B +
  • EN1175A/B

    Type of Adhesive: General Grade, low viscosity, two component solvent based(EA) polyurethane adhesive

    Application EN1175A/B is suitable for laminating :

    Pre-treated PE films

    Pre-treated PP films

    Pre-treated PET films

    Pre-treated PA films

    Metalized films, etc.

    Properties

    EN1175A/B is an economical adhesive for the general range of flexible packaging, it’s suitable to use for transparent lamination as well as for triplex lamination. EN1175A/B has good machine ability and a good wettability.

    Due to the low viscosity, EN1175A/B can be applied at very high solids content up to 45% which make the lower usage of EAC to reduce the manufacturing cost.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EN1175A EN1175B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 75±2 75±2
    Viscosity(mPa• s,25℃) 1500±300 2000±1000
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      150-200lines                            

    Application Solids                                           35-50%(recommend 40%)                

    Pot Life                                                            8hours by dynamic, 24hour by static       

    Dry Coating weight                                        2.0-3.5gsm                              

    Drying Section Temperature                       50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                             50~80℃ depending on films                 

    Cure Time(before slitting)                            24hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EN1175A(kg) EN1175B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 27.4 35 12~13
    20 4 21 40 13~14
    20 4 16 45 14~18
    20 4 12 50 19~21

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EN1175A is 20kg/drum, EN1175B is 4kg/drum.

    42            36

  • Plastic film, Plastic and Aluminum lamination,135C°EH6160A/B +
  • EH6160A/B

    Type of Adhesive: High Grade, two component solvent based(EA) polyurethane adhesive

    Application EH6160A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE films

    Pre-treated PP /CPP films

    Pre-treated PET films

    Pre-treated PA films,

    Unplasticized PVC films, etc.

    Properties

    EH6160A/B is recommended for high performance lamination. Beside its high heat resistance, it is used for flexible packages which are exposed to retorting(e.g. 135℃/30minutes). Especially for Film/Foil structure.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EH6160A EH6160B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 60±2 75±2
    Viscosity(mPa• s,25℃) 2500±1000 2000±1000
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      80-120lines                            

    Application Solids                                          25-40%(recommend 30%)                

    Pot Life                                                           8hours by dynamic, 24hour by static       

    Dry Coating weight                                       4.0-5.5gsm                              

    Drying Section Temperature                      50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                            50~80℃ depending on films                 

    Cure Time(before slitting)                           96hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EH6160A(kg) EH6160B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 36 25 13~15
    20 4 26 30 15~20
    20 4 18.9 35 20~28

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

     Package

    EH6160A is 20kg/drum, EH6160B is 4kg/drum.

    2                pic_06

  • Special for Aluminum laminationEM3075A/B +
  • EM3075A/B

    Type of Adhesive: Boiling Grade, two component solvent based(EA) polyurethane adhesive

    Application EM3075A/B is suitable for laminating :

    Pre-treated PE films

    Pre-treated PP films

    Pre-treated PET films

    Pre-treated PA films

    Metalized films,

    Cellophane,etc.

    Properties

    EM3075A/B specially perform excellent bond strength on film/Metalized film lamination. Transparent lamination can be pasteurized, boiled and sterilized.

    For laminating sterilization-proof film/Metalized film(e.g. 100℃/30minutes), we strongly recommend our

    EM3075A/B.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EM3075A EM3075B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 75±2 60±2
    Viscosity(mPa• s,25℃) 3500±1000 10-60
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      120-150lines                            

    Application Solids                                           25-40%(recommend 30%)                

    Pot Life                                                            8hours by dynamic, 24hour by static       

    Dry Coating weight                                        3.0-3.5gsm                              

    Drying Section Temperature                        50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                              50~80℃ depending on films                 

    Cure Time(before slitting)                              24hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EM3075A(kg) EM3075B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 45.6 25 12~13
    20 4 34 30 13~14
    20 4 25.7 35 15~16
    20 4 19.5 40 16~17

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EM3075A is 20kg/drum, EM3075B is 4kg/drum.

    15           14

  • Boiling and ReinforceEM3175A/B +
  • EM3175A/B

    Type of Adhesive: Boiling Grade, two component solvent based(EA) polyurethane adhesive

    Application EM3175A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE films

    Pre-treated PP films

    Pre-treated PET films

    Pre-treated PA films

    Metalized films, etc.

    Properties

    EM3175A/B specially perform excellent bond strength on film/Aluminum lamination. Transparent lamination can be pasteurized, boiled and sterilized.

    For laminating sterilization-proof film/film(e.g. 100℃/30minutes, vacuum bags), we strongly recommend our

    EM3175A/B.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EM3175A EM3175B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 75±2 75±2
    Viscosity(mPa• s,25℃) 3500±1000 3000±1000
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      120-150lines                            

    Application Solids                                           25-40%(recommend 30%)                

    Pot Life                                                            8hours by dynamic, 24hour by static       

    Dry Coating weight                                        3.0-3.5gsm                              

    Drying Section Temperature                       50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                             50~80℃ depending on films                 

    Cure Time(before slitting)                            24hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EM3175A(kg) EM3175B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 48 25 12~13
    20 4 36 30 14~15
    20 4 27.4 35 17~18
    20 4 21 40 21~22

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EM3175A is 20kg/drum, EM3175B is 4kg/drum.

    1.1           34

  • Common widely use ReinforceEN1075A/B +
  • EN1075A/B

    Type of Adhesive: General Grade, Two component solvent based(EA) polyurethane adhesive.

    Application EN1075A/B is suitable for laminating :

    Pre-treated PE films

    Pre-treated PP films

    Pre-treated PET films

    Pre-treated PA films

    Metalized films, etc.

    Properties

    EN1075A/B is an economical adhesive for the general range of flexible packaging, it’s suitable to use for transparent lamination as well as for triplex lamination. It can be applied at the high working solid which makes the product very economic. EN1075A/B has good machine ability and a good wettability.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EN1075A EN1075B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 75±2 75±2
    Viscosity(mPa• s,25℃) 2500±500 2000±1000
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                     120-180lines                            

    Application Solids                                          25-40%(recommend 35%)                

    Pot Life                                                            8hours by dynamic, 24hour by static       

    Dry Coating weight                                        2.0-3.5gsm                              

    Drying Section Temperature                       50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                             50~80℃ depending on films                 

    Cure Time(before slitting)                            24hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EN1075A(kg) EN1075B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 48 25 12~13
    20 4 36 30 13~14
    20 4 27.4 35 14~15
    20 4 21 40 16~17

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EN1175A is 20kg/drum, EN1175B is 4kg/drum.

    23             18

  • Fast Dry, Totally curied in 8-12 hoursEM3472A/B +
  • Instruction

    EM3472A/B is a two-component ethyl acetate soluble polyurethane adhesive designed for laminating aluminum foil and plastic film. It is suitable for vacuum supply, boiling, etc, in dry lamination of soft package.

    Function

    1. Lamination film has the features of good initial adhesion, high transparency, high peeling strength, etc.      
    2. It has a good performance of wetting to the film, and it’s especially good at coating process with economical efficiency.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.The Physical Nature of EM3472A and EM3472B

    Item

    EM3472A

    EM3472B

    Appearance

    Light yellow transparent liquid

    Colorless or light yellow transparent liquid

    Solid Content (%)

    72±2

    75±2

    Viscosity(mPa• s,25℃)

    2500±500

    2000±1000

    Solvent

    EAC

    EAC

    Mixing Ratio(Weight)

    20

    4

    Chart 2. The Changes of Solid Content and Viscosity during the Dilution

    EM3472A(kg)

    EM3472B (kg)

    EAC(kg)

    Solid Content (%)

    Viscosity,seconds

    (25℃,Zahn Cup #3)

    20

    4

    48

    25

    12~13

    20

    4

    36

    30

    13~14

    20

    4

    27.4

    35

    14~15

    20

    4

    21

    40

    16~17

    Attention: The moisture of EAC, no more than 300ppm, is the most suitable solvent for dry lamination. In addition, MEK, TO, ACETONE etc., whose moisture is no more than 300ppm, also can be used as solvent. It will reduce The effective content of hardener when there is active hydrogen, such as alcohol, amine, in the solvent.

    38                       26

  • Special for Aluminum and film laminationEM3072A/B +
  • EM3072A/B

    Type of Adhesive: Boiling Grade, two component solvent based(EA) polyurethane adhesive

    Application EM3072A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE films

    Pre-treated PP films

    Pre-treated PET films

    Pre-treated PA films

    Metalized films,

    Cellophane,etc.

    Properties

    EM3072A/B specially perform excellent bond strength on film/Foil lamination. Transparent lamination can be pasteurized, boiled and sterilized.

    For laminating sterilization-proof film/film(e.g. 100℃/30minutes), we strongly recommend our EM3072A/B.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item EM3072A EM3072B
    Appearance Light yellow Colorless or light yellow
    Solid Content (%) 72±2 75±2
    Viscosity(mPa• s,25℃) 5000±1000 2000±1000
    Solvent EAC EAC
    Mixing Ratio(By weight) 20 4
    Shelf Life 360days 300days

    Recommended Operating Conditions

    Application Method                                       Direct gravure                           

    Application Cylinder                                      120-150lines                            

    Application Solids                                           25-40%(recommend 30%)                

    Pot Life                                                             8hours by dynamic, 24hour by static       

    Dry Coating weight                                          3.0-3.5gsm                              

    Drying Section Temperature                          50~60℃/60~70℃/70~80℃(three section)     

    Laminating Temperature                                 50~80℃ depending on films                 

    Cure Time(before slitting)                                24hours(50±5℃)                         

    Dilution Table

    In order to obtain a certain solids, the following quantities of solvent(Ethyl Acetate) are recommended.

    EM3072A(kg) EM3072B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 45.6 25 12~13
    20 4 34 30 14~15
    20 4 25.7 35 17~18
    20 4 19.5 40 21~22

    Ethyl Acetate, Acetone and Methyl Ethyl Ketone provided that the water content does not exceed 300ppm. Aromatic and alcoholic solvents are not suitable.

    Package

    EM3072A is 20kg/drum, EM3072B is 4kg/drum.

    JYE3072A                  JYE3072B

     

    01                  25

  • Aluminum and Film lamination ReinforceEM3172A/B +
  • Instruction

    EM3172A/B is a two-component ethyl acetate soluble polyurethane adhesive designed for laminating aluminum foil and plastic film. It is suitable for vacuum supply, boiling, etc, in dry lamination of soft package.

    Function

    1. Lamination film has the features of good initial adhesion, high transparency, high peeling strength, etc.
    2. It has a good performance of wetting to the film, and it’s especially good at coating process with economical efficiency.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.The Physical Nature of EM3172A and EM3172B

    Item EM3172A EM3172B
    Appearance Light yellow transparent liquid Colorless or light yellow transparent liquid
    Solid Content (%) 72±2 75±2
    Viscosity(mPa• s,25℃) 5000±1000 2000±1000
    Solvent EAC EAC
    Mixing Ratio(Weight) 20 4

    Chart 2. The Changes of Solid Content and Viscosity during the Dilution

    EM3172A(kg) EM3172B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 45.6 25 12~13
    20 4 34 30 14~15
    20 4 25.7 35 17~18
    20 4 19.5 40 21~22

    Attention: The moisture of EAC, no more than 300ppm, is the most suitable solvent for dry lamination. In addition, MEK, TO, ACETONE etc., whose moisture is no more than 300ppm, also can be used as solvent. It will reduce The effective content of hardener when there is active hydrogen, such as alcohol, amine, in the solvent.

    31                      27

     

  • Common use and EconomicEM1075A/B +
  • Instruction

    EM1075A/B is a common and economic two-component ethyl acetate soluble polyurethane adhesive designed for general structure. This product is suitable for the lamination among PE, PP, PET and PA. It has good performance of lamination.

    Function

    1. Lamination film has the features of good initial adhesion, high transparency, high peeling strength, etc.
    2. It has a good performance of wetting to the film, and it’s especially good at coating process.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.The Physical Nature of EM1075A and EM1075B

    Item EM1075A EM1075B
    Appearance Light yellow transparent liquid Colorless or light yellow transparent liquid
    Solid Content (%) 75±2 75±2
    Viscosity(mPa• s,25℃) 2500±500 2000±1000
    Solvent EAC EAC
    Mixing Ratio(Weight) 20 4

    Chart 2. The Changes of Solid Content and Viscosity during the Dilution

    EM1075A(kg) EM1075B (kg) EAC(kg) Solid Content (%) Viscosity,seconds

    (25℃,Zahn Cup #3)

    20 4 48 25 12~13
    20 4 36 30 13~14
    20 4 27.4 35 14~15
    20 4 21 40 16~17

    Attention: The moisture of EAC, no more than 300ppm, is the most suitable solvent for dry lamination. In addition, MEK, TO, ACETONE etc., whose moisture is no more than 300ppm, also can be used as solvent. It will reduce The effective content of hardener when there is active hydrogen, such as alcohol, amine, in the solvent.

    19                                   5

  • Common Boiling useEM2175A/B +
  • Instruction

    EM2175A/B is a two-component ethyl acetate soluble polyurethane adhesive with high solid content and high transparency, can be used for the lamination among aluminum foil, PE,PP,PET and PA. It’s especially good at flexible package of dry lamination, such as plastic-plastic vacuum supply and so on. It 's suitable for  pasteurization

    Function

    1. Lamination film has the features of good initial adhesion, high transparency, high peeling strength, etc.
    2. It has a good performance of wetting to the film, and especially good at coating process with economical efficiency.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.The Physical Nature of EM2175A and EM2175B

    Item

    EM2175A

    EM2175B

    Appearance

    Light yellow transparent liquid

    Colorless or light yellow transparent liquid

    Solid Content (%)

    75±2

    75±2

    Viscosity(mPa• s,25℃)

    3500±1000

    3000±1000

    Solvent

    EAC

    EAC

    Mixing Ratio(Weight)

    20

    4

    Chart 2. The Changes of Solid Content and Viscosity during the Dilution

    EM2175A(kg)

    EM2175B (kg)

    EAC(kg)

    Solid Content (%)

    Viscosity,seconds

    (25℃,Zahn Cup #3),

    20

    4

    48

    25

    12~13

    20

    4

    36

    30

    14~15

    20

    4

    27.4

    35

    17~18

    20

    4

    21

    40

    21~22

    Attention: The moisture of EAC, no more than 300ppm, is the most suitable solvent for dry lamination. In addition, MEK, TO, ACETONE etc., whose moisture is no more than 300ppm, also can be used as solvent. It will reduce The effective content of hardener when there is active hydrogen, such as alcohol, amine, in the solvent.

    39            33

  • Boiling Resistance SL820A/B +
  • SL820A/B

    Type of Adhesive: Medium Grade, two component solvent free polyurethane adhesive

    Application SL820A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE

    Pre-treated PP

    Pre-treated PET

    Pre-treated LDPE

    Metalized Films., etc.

    Properties

    SL820 is an two component solvent free adhesive. Beside the lower coating weight and the high working speed , SL820 is excellent economic and efficient. Film/film package laminated by SL820 can be pasteurized, boiled and sterilized.

    For laminating sterilization-proof film/film(e.g. 100℃/40minutes), we strongly recommend our SL820A/B

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item SL820A SL820B
    Appearance Light yellow light yellow
    Solid Content (%) 100 100
    Viscosity(mPa• s,25℃) 2000±500 300±200
    Mix 100 85
    Density(g/cm3) 1.13 0.97
    Shelf Life 360days 360days

    Recommended Operating Conditions

    Application Method                                      Solvent free Machine                       

    Pot Life                                                           45minutes according to the circumstance   

    Dry Coating weight                                       0.8-2.0gsm                                

    Coating Temperature                                   30-40℃                                   

    Laminating Temperature                             35~50℃                                   

    Cure Time(before slitting)                             36hours(40±5℃)                         

    Package

    SL820A is 20kg/drum or 200kg/drum , SL820B is 17kg/drum or 170kg/drum.

     31                                 39

  • Plastic film lamination, can be boiled and steamed SL830A/B +
  • SL830A/B

    Type of Adhesive: High Grade, two component solvent free polyurethane adhesive

    Application SL830A/B is suitable for laminating :

    Aluminum Foil

    Pre-treated PE

    Pre-treated PP

    Pre-treated PET

    Pre-treated LDPE

    Metalized Films., etc.

    Properties

    SL830 is an two component solvent free adhesive. Beside the lower coating weight and the high working speed , SL830 is excellent economic and efficient. Film/film package laminated by SL830 can be pasteurized, boiled and sterilized.

    For laminating sterilization-proof film/film(e.g. 121℃/40minutes), we strongly recommend our SL830A/B

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item SL830A SL830B
    Appearance Light yellow light yellow
    Solid Content (%) 100 100
    Viscosity(mPa• s,25℃) 2500±500 500±300
    Mix 100 85
    Density(g/cm3) 1.13 0.97
    Shelf Life 360days 360days

    Recommended Operating Conditions

    Application Method                                       Solvent free Machine                       

    Pot Life                                                            No more than 30minutes according to the circumstance   

    Dry Coating weight                                        0.8-2.0gsm                                

    Coating Temperature                                    30-40℃                                   

    Laminating Temperature                              35~50℃                                   

    Cure Time(before slitting)                             48hours(40±5℃)                         

    Package

    SL830A is 20kg/drum or 200kg/drum, SL830B is 17kg/drum or 170kg/drum.

    pet-food                    lasirena

  • Function Adhesive SL840A/B +
  • Instruction

    SL840A/B is a two-component solvent free high performance polyurethane adhesive .It turns to be thin film full of elasticity when it is hardened absolutely. And it has good performance of lamination and heat sealing.

    Function

    1. It is suitable for kinds of plastic film lamination, such as OPP、CPP、LDPE、PET、PA、aluminized film、paper and so on.
    2. It has good performance of wetting to the film, and it’s especially good at coating process.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.the Physical Nature of SL840A and SL840B

    Item SL840A SL840B
    Appearance Yellow transparent liquid Yellow transparent liquid
    Solid Content (%) 100 100
    Viscosity

    (mPa• s,25℃)

    2500±500 1500±500
    Composition NCO OH
    Density(20℃,g/cm3) 1.12 1.10

    Attention

    • Please confirm it is suitable for laminating transparent ink.
    • Please confirm the appearance of the film is desirable when laminate PET printing.
    • Please confirm the products is non-corrosive before production.

    30      22

  • Common widely use Reinforce SL810A/B +
  • SL810A/B

    Type of Adhesive: General, two component solvent free polyurethane adhesive

    Application SL810A/B is suitable for laminating :

    Pre-treated PE

    Pre-treated PP

    Pre-treated PET

    Pre-treated LDPE

    Metalized Films., etc.

    Properties

    SL810 is an two component solvent free adhesive. Beside the lower coating weight and the high working speed , SL810 is excellent economic and efficient.

    It complied with US FDA 21 CFR175.105 .

    Typical specification

    Item SL810A SL810B
    Appearance Light yellow light yellow
    Solid Content (%) 100 100
    Viscosity(mPa• s,25℃) 1200±300 500±200
    Mix 100 85
    Density(g/cm3) 1.13 0.97
    Shelf Life 360days 360days

    Recommended Operating Conditions

    Application Method                                       Solvent free Machine                       

    Pot Life                                                            45minutes according to the circumstance   

    Dry Coating weight                                        0.8-2.0gsm                                

    Coating Temperature                                    30-40℃                                   

    Laminating Temperature                              35~50℃                                   

    Cure Time(before slitting)                              24hours(40±5℃)                         

    Package

    SL810A is 20kg/drum, SL810B is 17kg/drum.

    6            5

  • Function Adhesive SL850A/B +
  • Instruction

    SL850A/B is a two-component solvent free polyurethane adhesive .It turns to be thin film full of elasticity when it is hardened absolutely. And it has good performance of lamination and heat sealing.

    Function

    1. It is suitable for kinds of plastic film lamination, such as OPP,CPP,LDPE,PET,PA,aluminized film,paper and so on.
    2. It has good performance of wetting to the film, and it’s especially good at coating process.
    3. It conforms to the Food Hygiene Law of the P.R.C.
    4. It conforms to the Adhesive regulations for food packaging of China National Adhesives Industry Association.

    Physical Nature

    Chart 1.the Physical Nature of SL850A and SL850B

    Item

    SL850A

    SL850B

    Appearance

    Yellow transparent liquid

    Yellow transparent liquid

    Solid Content (%)

    100

    100

    Viscosity

    (mPa• s, 25℃)

    2500±500

    1000±500

    Composition

    NCO

    OH

    Density(20℃,g/cm3)

    1.12

    1.10

    Attention

    • Please confirm it is suitable for laminating transparent ink.
    • Please confirm the appearance of the film is desirable when laminate PET printing.
    • Please confirm the products is non-corrosive before production.

    11             08

  • Sealed Auto Light PUR JUR-624 +
  • Item JUR-624
    Appearance Black solid
    Solid Content (%) 100
    Viscosity(mPa• s) 12000 (120℃)
    Usage Seal for Auto light
    Characteristic It has good heat resistance, elasticity and anti-aging and fast hard

     

    6          5

  • Fabric and Film, fabric and fabric lamination and EVA Lamination JUR-627 +
  • Instruction

    JUR-627 is a reactive hot melt adhesive which is High Initial Strength based on polyurethane for lamination of textiles as fabric, EVA and TPU film.

    This product has been formulated to give very high initial strength, excellent final strength, wash-cleaning resistance and good flexibility after final curing.

    Technical Product Data

    The  Technical Product Data of JUR-627

    Item

    JUR-627

    Appearance

    High thick semi solid

    Solid Content (%)

    100

    Viscosity(mPa• s)

    2,000 mPa.s approx(90°C)

    Density

    1.15-1.18g/ cm3 @ 25°C approx

    Suggested Application Temperature

     90 - 120°C (short-term 140°C), suggest 100°C

    Application Method

    Nozzle or coating roller systems

    Open Time

    Depends on procedure, temperature and substrate, but typically ca. 10 minutes

    Application Notes:

    1. Special for PUR adhesive and coating equipment to carry on construction are recommended. After construction, the equipment should be cleaned. And the rest hot melt is tightly sealed in order to  ensure the normal use for next time.

    2. After coating, the valid using time of glue  has a close relationship with the temperature of glue and operating environment, the heat conductivity of material and the temperature of material itself.

    3. The rate of curing depends on the coating thickness, environment temperature, humidity and permeability of materials.

  • PVC and Wood PUR JUR-623 +
  • Instruction

    JUR-623 is high stickiness and high initial strength. It imitates Kleiberit (Ke Libao) 707 Series from Germany, used to PVC veneer or edge on furniture. 

    Technical Product Data

    The  Technical Product Data of JUR623

    Item

    JUR623

    Appearance

    White solid 

    Solid Content (%)

    100

    Viscosity(mPa• s)

    150,000±1,000(120℃)

    Density

    1.18g/ cm3 @ 25°C approx

    Suggested Application Temperature

    120°C-140°C (140°C are recommended)

    Positioning Time

    3~5s  (120℃ gluing, 0.3mm glue film,25℃ environmental temperature)

    Moisture Curing Rate

    1-3days (0.5mm glue film, 25℃ environmental temperature, 40-70% humidity)

    Application Notes:

    1. Special for PUR adhesive and coating equipment to carry on construction are recommended. After construction, the equipment should be cleaned. And the rest hot melt is tightly sealed in order to  ensure the normal use for next time.

    2. After coating, the valid using time of glue  has a close relationship with the temperature of glue and operating environment, the heat conductivity of material and the temperature of material itself.

    3. The rate of curing depends on the coating thickness, environment temperature, humidity and permeability of materials.

    wood     7

  • Fabric and Fabric lamination and EVA Lamination JUR-626 +
  • Instruction

    JUR-626 is a reactive hot melt adhesive which is High Initial Strength based on polyurethane for lamination of textiles. This product has been formulated to give very high initial strength, excellent final strength, wash-cleaning resistance and good flexibility after final curing.

    Product benefits:

    Very good tack and initial strength

    High final strength after curing

    Good flexibility

    Excellent wash-cleaning resistance

    Broad adhesion spectrum

    Chart The  Technical Product Data of JUR626

    Item JUR626
    Chemical Base Polyurethane reactive hot melt
    Appearance White Solid
    Solid Content (%) 100
    Viscosity(mPa• s) 100°C 50, 000 mPa.s approx.

    110°C 28, 000 mPa.s approx.

    120°C 15, 000 mPa.s approx.

    130°C 10,000 mPa.s approx.

    140°C  6,5000 mPa.s approx.

    Density 1.18g/ cm3 @ 25°C approx
    Suggested Application Temperature 120°C-140°C (140°C are recommended)
    Open Time Depends on procedure, temperature and substrate, but typically ca. 5~10 minutes
    Application Method  Nozzle or coating roller systems

    Health and Safety :

    To minimise the risk of burns, the use of eye protection and protective clothing is recommended when working near a hot melt applicator. To minimise the risk of flammable vapours, do not exceed a melt temperature of 200 °C.

    1                 9

  • Metal and TPU Hot Melt JUR-622 +
  • Item JUR-622
    Appearance Light yellow transparent solid
    Solid Content (%) 100
    Viscosity(mPa• s) 5000 (120℃)
    Usage Adhesive for Metal and plastic
    Characteristic It has good adhesion for metal

     

    metal hot melt1                   12

  • Paper and Plastic Film or Paper and Aluminum Lamination JUR-625 +
  • Instruction

    JUR-625 is a reactive hot melt which is non-toxic and solvent free adhesive based on polyurethane for lamination of paper and plastic. The product has been formulated to give very high initial strength, high transparency and fast hard.

    Function

    1. It is colorless and solvent free PUR which is environmental and non-toxic.

    2. It has the features of good tack and initial strength, good stability.

    Physical Nature

    Chart 1.The  Technical Product Data of JUR625

    Item

    JUR625

    Appearance

    Light yellow transparent liquid

    Solid Content (%)

    100

    Viscosity(mPa• s)

     650(90℃);  1000  (80℃)

    Density

    1.18g/ cm3 @ 25°C approx

    Suggested Application Temperature

    80°C-110°C (90°C are recommended)

    Open Time

    30mins

    Moisture Curing Rate

     Depends on temperature and humidity,

    the curing process should be 6-12 hours.

    Application Notes:

    1. Special for PUR adhesive and coating equipment to carry on construction are recommended. After construction, the equipment should be cleaned. And the rest hot melt is tightly sealed in order to  ensure the normal use for next time.

    2. After coating, the valid using time of glue  has a close relationship with the temperature of glue and operating environment, the heat conductivity of material and the temperature of material itself.

    3. The rate of curing depends on the coating thickness, environment temperature, humidity and permeability of materials.

    10            12

  • Auto Interior and Appliances PUR JUR-621 +
  • Instruction

    JUR621 Auto Interior and Appliances PUR, has  Fast hard, high initial adhesion, good positioning effect, sag resistant. It can be used for plastic fittings and Auto interior parts.

    Specifications

    Solid Content            100%

    Viscosity                   3000mPa.s(120℃)

    Apperance               Milky white solid

    Density                    1.8g/cm3

     

    2              5

     

  • Bright PU Adhesive JY-945D +
  • Instruction

    JY-945D bright PU resin, DMF and heavy metal free. It can be printed to garments, textile fabric and coating fabric. It has advantage of viscose, nylon fabrics, knitted fabrics, chemical fiber and cotton cloth, soft, dry fast, washable.

    1. Specifications:

    Solid components: 50%

    Appearance: Slightly yellow transparent liquid

    Viscosity: 100000-150000 CPS/25 ℃

    Tensile strength: 400-500 kg/cm2

    2. Attention: Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: Normal storage conditions, save for one year;

    5. Use: Note exhaust ventilation;

    6. Package: 200 KGS / DRUM
    PU2                    matte PU00

  • Embossing Adhesive JY-2030 +
  • Instruction

    JY-2030 special embossing resin, used in clothing, fabric and coating. It has the effects of strong sense of stereoscopic, soft to the touch, excellent of environmental protection, color scattered and resistance of swelling.

    1. Specifications:

    Solid components: 30 ± 2%
    Ingredients: Nylon polyester resin
    Viscosity: 60000-90000 CPS/25 ℃
    Solvent: MEK, TOL
    Tensile strength: 200-400 kg/cm2

    2. Attention:
    1) The use of solvents to control the moisture content of the request are as follows:
    MEK          0.1% below
    2) Solvent moisture content too high, substantial impact on quality;
    3) Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: Normal storage conditions, save for one year;

    5.Use: Note exhaust ventilation;

    6. Package: 200 KGS / DRUM

    2                0

  • Strong Adhesive JY-699 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-699 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Soft Smoke Adhesive Washable JY-4700 +
  • Instruction

    JY-4700 soft bright smoke resin, has high-brightness, good fastness. It is good adhesive to nylon fabrics, knitted fabrics, chemical fiber and cotton cloth, soft, dry fast, immediately foil separated.

    1. Specifications:

    Solid components : 60 ± 1%
    Appearance : slightly yellow transparent liquid
    Viscosity : 70000-80000 CPS/25 ℃
    Solvent : EAC / MEK
    Tensile strength : 30-50 kg/cm2
    Elongation : 100-300%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: Normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 15 KGS / DRUM or 200 KGS / DRUM

    Fabric           matte pu0

  • Water-based Elasticity Adhesive GPC-7110 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-7110 35±2 1000-2000 100--120
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    7 - - Waterborne PU resin for gold stamp
  • Elasticity Strong Smoke Chemical on foil JY-9270 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-9270 70±2 8-12 -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥800 - Gold stamp adhesive with high requirements
  • Common Smoke Adhesive JY-380 +
  • Instruction

    JY-380 Smoke resin, has high-brightness, good fastness. It can be glued to nylon fabrics, knitted fabrics, chemical fiber and cotton cloth, soft, dry fast, immediately stripped.

    1. Specifications:

    Solid components: 50 ±5%

    Appearance: Slightly yellow transparent liquid
    Viscosity: 5000-10000 CPS/25 ℃
    Solvent: TOLUENE / MEK
    Tensile strength: 30-50 kg/cm2

    Elongation: 100-300%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: normal storage conditions, save for one year;

    5. Use: Note exhaust ventilation;

    6. Package: 15 KGS / DRUM  or 200 KGS / DRUM
    IMG_7780               5

     

  • PU Adhesive JY-8030 +
  • Instruction

    JY-8030 PU resin, used in clothing, fabric and coating. It has the effects of strong sense of
    stereoscopic, soft to the touch, excellent of environmental protection, color scattered and
    resistance of swelling.

    1. specifications:

    solid components: 30 ± 2%
    Ingredients : PU
    Viscosity : 120000-90000 CPS/25 ℃
    Solvent : DMF,MEK
    Tensile strength : 200-400 kg/cm2

    2. Attention:
    1) the use of solvents to control the moisture content of the request are as follows:
    MEK 0.1% below
    2) solvent moisture content too high, substantial impact on quality;
    3) complete with sealed to prevent infiltration of water vapor;
    3. storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. save: normal storage conditions, save for one year;
    5. use: Note exhaust ventilation;
    6. package: 200 KGS / DRUM

    19                            6

  • Shrink Adhesive JY-650 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-650 65±2 8--12 -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥600 - Gold stamp adhesive,dry fast,good fastness
  • Strong PU Adhesive JY-945A +
  • Instruction

    JY-945A bright PU resin, DMF and heavy metal free. It can be printed to garments, textile fabric and coating fabric. It has advantage of viscose, nylon fabrics, knitted fabrics, chemical fiber and cotton cloth, soft, dry fast, washable.

    1. Specifications:

    Solid components: 50%

    Appearance: Slightly yellow transparent liquid

    Viscosity: 100000-150000 CPS/25 ℃

    Tensile strength: 400-500 kg/cm2

    2. Attention: Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: Normal storage conditions, save for one year;

    5. Use: Note exhaust ventilation;

    6. Package: 200 KGS / DRUM

    1                    1

  • Super-Bright Reflect Printing Adhesive JY-803 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-803

    0.25-0.36
    - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - -

    Composite high reflective material
  • Matte PU Adhesive JY-8501 +
  • Instruction

    JY-8501 matte coating resin, used in clothing, fabric and coating. It has the effects of strong sense
    of dermis, matte, ma stereoscopic, soft to the touch, excellent of environmental protection,
    color scattered and resistance of swelling.

    1. Specifications:

    Solid components: 35 ± 2%
    Viscosity : 11000-90000 CPS/25 ℃
    Solvent : MEK, TOL
    Tensile strength : 400-500 kg/cm2

    2. Attention:
    1) The use of solvents to control the moisture content of the request are as follows:
    MEK 0.1% below
    2) Solvent moisture content too high, substantial impact on quality;
    3) Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: Normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 200 KGS / DRUM

    19                                 5

  • Water proof Adhesive JY-108 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-108 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Economy Chemical on foil JY-750 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-750 70±2 8--12 -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥600 -

    Gold stamp adhesive toughnes
  • Elasticity Chemical on foil JY-9058 +
  • Instruction

    JY-9058bright high-elasticity foilprinting resin, has high solid components, brightness, good
    fastness. It can be printed to viscose, nylon fabrics, knitted fabrics, chemical fiber and cotton
    cloth, soft, dry fast, washable.

    1. Specifications:

    Solid components: 70%
    Appearance : Slightly yellow transparent liquid
    Viscosity : 80000-100000 CPS/25 ℃
    Solvent : TOLUENE / MEK
    Tensile strength : 300-500 kg/cm2
    Elongation : 500-800%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 200 KGS / DRUM

    11                                 5

  • Smoke Resin Additive JY-4000 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-4000 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Water-based Non-yellowing Lamination GPC-50 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-50 50±2 0.1--0.5 40±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 - water-base, non yellowing
  • Soft and Super Washable SA-9165 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-9165 65±2 8--15 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 - High-grade fabric and breathable film adhesive
  • Non-yellowing Garment Lamination SA-2060 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-2060 60±2 3--5 25±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥500 - Non yellowing and wash resistance
  • Economy Standard Home Textile Adhesive SA-9065 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-9065 63±2 13--18 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥35 ≥550 - General economy

    SA-9065 fabric lamination resin has high solid components, strong. It can be laminated to nylon fabrics, knitted fabrics, chemical fiber, PU and suede and so on, good effect, dry fast, Mid-hard feel, special used to home textile lamination.

    1.specifications: solid components: 65±3%

                                          Appearance   : slightly yellow transparent liquid
                                          Viscosity         : 180000-150000 CPS/25 ℃
                                         Solvent           : TOLUENE / MEK/DMF
                                         Tensile strength     : 200-150 kg/cm2

                                        Elongation        : 400-700%

    2.Description:

                                                 Summer                                Winter
           SA-9065                          100                                     100

    Connector(LA-75)              8-11                                     10-13

    Accelerant(LA-90)              1-3                                        3-5

    MEK                                    10-40                                  10-30

    According fabric necessary adjustments to your viscosity

     

    3.Attention: complete with sealed to prevent infiltration of water vapor;

    4.storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    5.save: normal storage conditions, save for one year;

    6.use: Note exhaust ventilation;

    7.package: 200 KGS / DRUM

  • Solvent-free Homoeothermy Lamination SA-100B +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-100B 100 0.3--0.5 30±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 - No solvent, Hydrolysis resistance
  • High Solid Content Soft PU Lamination SA-2270 +
  • Instruction

    SA-2270 Harmless PU Lamination Resin has high solid components, strong. It can be glued to
    nylon fabrics, knitted fabrics, chemical fiber, PU and suede and so on, good effect, soft, dry
    fast. After completely dried, may reach the export standard.

    1. Specifications:

    Solid components: 65±3%
    Appearance : Slightly yellow transparent liquid
    Viscosity : 150000-130000 CPS/25 ℃
    Solvent : TOLUENE / MEK /DMF
    Tensile strength : 200-450 kg/cm2
    Elongation : 400-700%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3.Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: Normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 200 KGS / DRUM
    87

  • TPU PVC and PTFE Adhesive SA-9062 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-9062 65±2 3--5 -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥600 - TPU、PVC、PTFE adhesive
  • Solvent-free Homoeothermy Lamination SA-100A +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-100A 100 2--5 30±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 - No solvent,Hydrolysis resistance
  • Soft and Washable for Clothing Lamination SA-9011 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-9011 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • High Washable Garment Lamination SA-3060 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-3060 60±2 6--8 10±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥600 - Wash resistance and moisture permeability

    Wash

  • No Sticky and Bright PVC Lamination SA-9065 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-9045 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -

     

  • Strong Home Textile Lamination SA-9068 +
  • Instruction

    SA-9068 fabric lamination resin has high solid components, strong. It can be laminated to nylon
    fabrics, knitted fabrics, chemical fiber, PU and suede and so on, good effect, dry fast, hard feel,
    special used to home textile lamination.

    1. Specifications:

    Solid components: 65±3%
    Appearance : Slightly yellow transparent liquid
    Viscosity : 180000-150000 CPS/25 ℃
    Solvent : TOLUENE / MEK
    Tensile strength : 200-150 kg/cm2
    Elongation : 400-700%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 200 KGS / DRUM

    9                      19

  • Water-based Lamination GPC-603 +
  • Instruction

    GPC-603 is an anionic polyurethane resin for lamination. It is washable, solvent resistance, adhesion fastness, suitable for fabrics and yarns lamination.

    1. Specifications:    

    Solid components: 50±1%

    Appearance: Milky white
    Viscosity: <1000 CPS/25 ℃
    PH: 7

    2. Attention:
    1). Complete with sealed to prevent infiltration of water vapor;

    2). Do not pour the used resin into the unused unless test.

    3). The mixed resin with connector should be used out in 8 hours or else the mixture would be hard.

    3. Storage: Please placed in a cool dry place and avoid direct sunlight;

    4. Save: Normal storage conditions, save for 6 months;

    5. Package: 50 KGS / DRUM or 100 KGS / DRUM
    pu              9

  • Water-based Bright Coating Adhesive GPC-880 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-880 35±2 200-400 30-50
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    6--8 - - Good adhes ion,film sense,the light for textile coating
  • Soft and Two-Gomponent JYT-9050 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-9050 50±2 10--16 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥10 ≥500 DMF、MEK、TOL Soft, Two component

     

  • Soft Two-component after adhesive JYT-9060 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-9060 60±2 10--16 10±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥500 DMF、MEK、TOL Soft, Two component for adhesive
  • Water-based Rocking Adhesive GPC-602 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-602 50±2 200-500 -
    PH Tensile streng (Mpa) Tensile streng (Mpa) Characteristicsand application
    6--8 ≥6 - High solid waterborne PU RESIN
  • Strong and High Bright JYT-8100 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8100 30±2 6--14 100±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥45 ≥400 DMF、MEK、TOL Hard, good bright

     

  • Water-based Coating Adhesive GPC-201 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-201 50±2 200-500 10-15
    PH Tensile streng (Mpa) Solvents Characteristicsand application
    6--8 - - High solid waterborne PU coating adhesive
  • Soft Water Pressure Resistance and No Sticky JYT-950A +
  • Instruction

    JYT-950A is soft one-component base PU resin with performance of high soft quality, water pressure resistance, good adhesion. It can be used in waterproof coating.

    1. Specifications:  

    Appearance: Colorless or light yellow transparent liquid

    Solid Content(%): 50±1%

    Viscosity(CPS/25 ℃): 60,000-80,000

    100% Modulus(MPa) : 2.5±0.5

    Tensile strength(MPa): ≥15

    Elongation: ≥600%

    Solvent: DMF/ MEK/TOL

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: Normal storage conditions, save for 6 months;
    5. Use: Note electrostatic ecluded and exhaust ventilation;
    6. Package: 200 KGS / DRUM

  • Soft and Water Pressure Resistance Base Adhesive JYT-940 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-940 40±2 8--14 30±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF、TOL Super soft,Better avulse
  • Super Soft and Extinction JYT-8020 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8020 30±2 6--14 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥35 ≥550 DMF、MEK、TOL Super soft and matte type
  • Water-based Flame Coating Adhesive GPC-157 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-157 30±2 200-400 20-40
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    6--8 - - Soft,good elasticity,for textile flame retardant coating
  • Mid-hard and Thixotropic JYT-8080 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8080 30±2 6--14 70±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 DMF、MEK M-hard,touch-changing
  • Soft 1.5 Component Water Pressure Resistance JYT-9061 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-9061 60±2 10--16 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥300 DMF、MEK、TOL Soft, 1.5 component for adhesive, good waterproof
  • Water-based Flocking Adhesive GPC-603 +
  • Instruction

    GPC-603 is an anionic polyurethane resin for lamination. It is washable, solvent resistance, adhesion fastness, suitable for fabrics and yarns lamination.

    1. Specifications:  

    Solid components: 50±1%

    Appearance: Milky white
    Viscosity: <1000 CPS/25 ℃
    PH: 7

    2. Attention:
    1). Complete with sealed to prevent infiltration of water vapor;

    2). Do not pour the used resin into the unused unless test.

    3). The mixed resin with connector should be used out in 8 hours or else the mixture would be hard.

    3. Storage: Please placed in a cool dry place and avoid direct sunlight;

    4. Save: normal storage conditions, save for 6 months;

    5. Package: 50 KGS / DRUM or 100 KGS / DRUM
    6             19

  • Soft and One-Component Base Adhesive JYT-930 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-930 30±2 8--14 25±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥25 ≥600 DMF、TOL Soft type,one component for adhesive
  • Water-based Dry Coating Adhesive GPC-305c +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-305C 30±2 100-200 90--100
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    6--8 - - Waterborne PU resin for dry veneer
  • Soft and Thixotropic JYT-8050 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8050 30±2 6--14 50±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥550 DMF、MEK、TOL Soft, touch-changing
  • Water-based Coating Adhesive GPC-600 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-600 45±2 500-1000 15-20
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    6--8 - - Waterborne PU achesive of Vacuum plastic suction
  • Soft and One-Gomponent JYT-945 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-945 45±2 8--14 40±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥20 ≥550 DMF、TOL Hard type, one component for adhesive
  • Ultra Hard and Bright JYT-8300 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8300 30±2 2--12 300±20
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥200 DMF、MEK Super hard,better bright
  • Soft Two-component after adhesive JYT-9060 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-9060 60±2 10--16 10±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥500 DMF、MEK、TOL Soft, Two component for adhesive
  • Super Soft and No Sticky JYT-8010 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8010 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Water-based Matte Coating Adhesive GPC-108 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPC-108 35±2 200-400 30-50
    PH Tensile streng (Mpa)

    Active temperature(℃)
    Characteristicsand application
    6--8 - - Good adhesion,film sense,the matting for textile coating
  • Soft and Compatible with PA JYT-8035 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8035 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Water Pressure Resistance JYT-8030 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYT-8030 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Mid-hard Foil Use Surface Adhesive JYF-3000TR +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-3000TR 30±2 4--5 80±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥35 ≥500 DMF、TOL、IPA、MEK Waterproof and moisture permeable for topping transfer film
  • High Solid Content Water Pressure Resistance Base Adhesive JYF-3060BR +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-3060BR 60±2 5--6 15±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≤10 ≥500 DMF、TOL、IPA waterproof and moisture permeable for basic high solid

     

  • Mid-soft Matt Direct Coating Surface Adhesive JYF-5430T +
  • Instruction

    JYF-5430T, a mid-soft hydrophilic high moisture permeability of polyurethane adhesive, used as surface coating resin after base resin, suitable for direct coating.

    1. Specifications:

    Appearance: Milky white liquid

    Solid components: 30 ± 1%
    Viscosity: 20000-30000 CPS/25 ℃
    Solvent: TOL, DMF, IPA
    Tensile strength  : 30-45 MPa

    2. Attention:
    1) The use of solvents to control the moisture content of the request are as follows:
    MEK 0.1% below
    2) Solvent moisture content too high, substantial impact on quality;
    3) Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: normal storage conditions, save for six months;

    5. Package: 180 KGS / DRUM

    matte PU                   matte pu0

  • Foil Use Surface Adhesive JYF-3070R +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-3070R 30±2 5--6 60±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥500 DMF、TOL、IPA Waterproof and moisture permeable for topping, transfer film
  • Wet PU adhesive JYF-7000W +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-7000W 20±2 8--10 50±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥500 DMF Wet pu resin, waterproof and moisture permeable
  • Basic Water Pressure Resistance JYF-3010B +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-3010B 40±2 5--7 10±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≤10 ≥600 TOL、IPA、MEK Water-roof, and moisture permeable for basic
  • Soft Cold-resistance Base Adhesive JYF-5450B +
  • Instruction

    JYF-5450B, a hydrophilic non-pass high moisture permeability of polyurethane adhesive, used as direct primer coating resin.

    1. Specifications:

    Appearance: Light yellow liquid

    Solid components: 45 ± 1%
    Viscosity: 50000-60000 CPS/25 ℃
    Solvent: TOL, MEK, IPA
    Tensile strength  : 30-45 MPa
    2. Attention:
    1) The use of solvents to control the moisture content of the request are as follows:
    MEK          0.1% below
    2) Solvent moisture content too high, substantial impact on quality;
    3) Complete with sealed to prevent infiltration of water vapor;

    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;

    4. Save: normal storage conditions, save for six months;

    5. Package: 180 KGS / DRUM
    19                     20

  • High Solid Content Water Pressure Resistance Base Adhesive JYF-2000BR +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-2000BR 53±2 5--6 10±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≤10 ≥500 DMF、TOL、IPA、MEK Water-roof and moisture permeable for high solid
  • Surface Extinction Adhesive JYF-3020T +
  • Articles Solid  Content(%) Viscosity(X104Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-3020T 30±2 2--4 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF、TOL、IPA、MEK Water-roof, and moisture permeable for topping,deluster
  • Soft and Hydrolysis-resistance JY-6025HR +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-6025HR 30±2 4--10 30±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥60 ≥600 DMF Soft, better avulse excellent hydrolysis resistance
  • Mid-Soft and Hydrolysis-resistance JY-6040HR +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-6040HR 30±2 10--16 40±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥45 ≥600 DMF M-soft, excellent hydrolysis resistance, high density process
  • Mid-Hard and Hydrolysis-resistance JY-6075HR +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-6075HR 30±2 4--10 75±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥500 DMF M-hard, better avulse excellent hydrolysis resistance
  • Mid-Hard and Hydrolysis-resistance JY-6065HR +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-6065HR 30±2 10--16 60±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥50 ≥500 DMF M-hard, excellent hydrolysis resistance, high density prosess
  • Abrasion and Silicon free JY-7308 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7308 30±2 16-20 45±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF Super Soft,Like muscle, no silicone
  • Super-soft and Good Forming JY-7050C +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7050C 30±1 12--18 45±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥600 DMF  Middle soft good volume for Glove,better avulse
  • Super-soft and Good Forming JY-7015 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7015 30±1 12--18 15±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF Super Soft,Like muscle,for cloth
  • Abrasion and Silicon free JY-7304G +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7304G 30±2 16--20 45±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF Super Soft,Like muscle,contain silicone
  • Abrasion and Silicon free JY-7302G +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7302G 30±2 16-20 25±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF Super Soft,Like muscle,no silicone
  • Super-soft and Good Forming JY-7020C +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JY-7020C 30±1 12--18 20±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥30 ≥600 DMF Super Soft,Like muscle,for Glove
  • Soft JYF-8020 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-8020 30±2 6--10 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥40 ≥500 DMF,MEK For soft,good touch feeling
  • Soft Foam Adhesive JYF-9015 +
  • Articles Solid  Content(%) Viscosity(X10^4Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-9015 70±2 6--10 20±10
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥20 ≥200 DMF、MEK For  soft high solid content,foam type
  • Soft JYF-8035 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    JYF-8035 30±2 6--10 20±5
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    ≥45 ≥500 DMF、MEK For soft,good touch feeling
  • Water-based Shoe Adhesive GPU-18 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPU-18 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - -
  • Water-based Shoe Adhesive GPA-100 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    GPA-100 50±2 4000-6000 -
    PH Tensile streng (Mpa) Active temperature(℃) Characteristicsand application
    7--8 - 65-75 Waterborne PU achesive of shoes
  • Standard Accelerant LA-90 +
  • Instruction

    LA—90 accelerant is the polyurethane fast atalyst classified in the metal salts. It has
    high-brightness, good fastness, save accelerating time. It can be glued to nylon fabrics, knitted
    fabrics, chemical fiber and cotton cloth, soft, dry fast, washable, applicable wrinkling,
    foilprinting.

    1. Specifications:
    Appearance : transparent liquid
    Solvent : TOLUENE

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: Normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 15 KGS / DRUM

  • Harmless Brighter SA-100 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-100 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Environmental friendly catalyst
  • Standard Connector LA-75 +
  • Instruction

    LA-75 connector is the polyurethane agent which has NOC-group, is one of the excellent
    products more than 10 years. It has extra good curing effect. It can be glued to nylon fabrics,
    knitted fabrics, chemical fiber and cotton cloth, soft, dry fast, washable.

    1. specifications:

    Solid components: 75%
    Appearance : Slightly yellow transparent liquid
    Solvent : Ethyl Acetate
    Viscosity : 7500-12500 CPS/25 ℃
    NCO% : 12.5±0.5%

    2. Attention: Complete with sealed to prevent infiltration of water vapor;
    3. Storage: Please placed in a cool dry place and avoid direct sunlight and away from fire;
    4. Save: normal storage conditions, save for one year;
    5. Use: Note exhaust ventilation;
    6. Package: 20 KGS / DRUM

  • Non-yellowing Hardener NA-75 +
  •  

    Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    NA-75 75±2 0.1-0.3 -
    Tensile streng (Mpa) NOC content(%) Solvents Characteristicsand application
    - 18.5±1 - Non yellowing hardener
  • Standard Brighter SA-90 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-90 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Standard type catalys
  • PA Coating and Calendering Connector LA-70 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    LA-70 70±2 0.3-0.5 -
    Tensile streng (Mpa) NOC content(%) Solvents Characteristicsand application
    - 12.5±1 EAC Standard hardener
  • MELAMINE Brighter SA-10 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-10 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Amino  catalyst
  • Strong Enhancer Agent SA-500 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-500 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Fastness improver
  • Abrasion Agent SA-108 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-108 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Abrasion resistant agent
  • Hot-resistance Hardener SA-55 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-55 55±2 - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Amino hardener
  • Sub-water Agent SA-150 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-150 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Surfactant
  • Dry Fast SA-120 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-120 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Quick dry
  • Hardener SA-75 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-75 75±2 0.4-0.6 12.5±1
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - EAC Standard hardener
  • Non-yellowing Hardener NA-100 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    NA-100 100±2 0.2-0.4 -
    Tensile streng (Mpa)

    NOC content(%)
    Solvents Characteristicsand application
    - 22±1 - Non-yellowing Hardener
  • Slip Agent SA-107 +
  • Articles Solid  Content(%) Viscosity(X10Cps/25°C) 100% ModuI us  (kg/cm2)
    SA-107 - - -
    Tensile streng (Mpa) Elongation(%) Solvents Characteristicsand application
    - - - Slip agent
Our products drums